Long-term durability of red mud-modified cement mortars: Effects of high temperature and freeze-thaw cycles
DOI:
https://doi.org/10.20528/cjsmec.2025.03.001Keywords:
red mud, waste materials, physico-mechanical properties, high temperature, freeze-thaw, SEM-EDXAbstract
The use of industrial by-products such as red mud in cementitious materials addresses sustainability by reducing environmental impact and improving performance. As a hazardous waste from aluminium production, red mud offers a promising solution for waste management and improves the mechanical and durability properties of mortar when used as a partial cement replacement. This study investigates the long-term mechanical and durability properties of cement mortars modified with red mud, a by-product of alumina production. Red mud was incorporated at substitution percentages of 5%, 10%, 15%, 20%, 25%, 30% and 35% by weight of cement. The mortars were subjected to harsh environmental conditions such as high temperatures (200°C to 600°C), freeze-thaw cycles (50 and 100 cycles), and normal curing conditions at 365 days of age. The study showed that partial replacement of cement with red mud significantly affected the mechanical and durability properties of the mortars. The optimum red mud replacement level of 10% showed that microstructural compactness and hardness were improved by increasing the ultrasonic pulse velocity, dynamic modulus of elasticity and flexural strength. Durability tests showed improved thermal resistance at moderate levels of red mud content, while higher levels adversely affected freeze-thaw performance. These findings confirm that a 10% red mud substitution offers the best balance between strength, durability, and sustainability.
Author Biography
-
Ibrahim A. Alameri , Emirates International University
Ibrahim A. Alameri
https://www.linkedin.com/in/ibrahim-alameri/
Sana’a University Emirates International University
Yemen
References
Aboalella, A. A., & Elmalky, A. (2023). Use of crushed bricks and recycled concrete as replacement for fine and coarse aggregates for sustainable concrete production. Challenge Journal of Concrete Research Letters, 14(2), 39–46.
Ai, T., Zhong, D., Zhang, Y., Zong, J., Yan, X., & Niu, Y. (2021). The effect of red mud content on the compressive strength of geopolymers under different curing systems. Buildings, 11(7), Article 298. https://doi.org/10.3390/buildings11070298
Alameri, I. A., & Oltulu, M. (2020). The physico-mechanical properties of concrete with red mud at high temperatures. Challenge Journal of Concrete Research Letters, 11(4), 82–91.
Anirudh, M., Rekha, K. S., Venkatesh, C., & Nerella, R. (2021). Characterization of red mud based cement mortar; mechanical and microstructure studies. Materials Today: Proceedings, 43, 1587–1591. https://doi.org/10.1016/j.matpr.2020.09.635
ASTM International. (2015). Standard test method for resistance of concrete to rapid freezing and thawing (ASTM C666 / C666M – 15). West Conshohocken, PA.
ASTM International. (2017). Standard practice for measuring ultrasonic velocity in materials (ASTM E494 – 95). West Conshohocken, PA.
Bergonzoni, M., Melloni, R., & Botti, L. (2023). Analysis of sustainable concrete obtained from the by-products of an industrial process and recycled aggregates from construction and demolition waste. Procedia Computer Science, 217, 41–51. https://doi.org/10.1016/j.procs.2022.12.200
Díaz, B., Freire, L., Nóvoa, X. R., & Pérez, M. C. (2015). Chloride and CO2 transport in cement paste containing red mud. Cement and Concrete Composites, 62, 178–186. https://doi.org/10.1016/j.cemconcomp.2015.02.015
Gao, Y., Li, Z., Xin, G., Shen, Q., Zhang, J., & Yang, Y. (2023). Utilization of high-volume red mud application in cement-based grouting material: Effects on mechanical properties at different activation modes. Journal of Materials in Civil Engineering, 35(4), Article 04023011. https://doi.org/10.1061/JMCEE7.MTENG-14442
Gou, M., Hou, W., Zhou, L., Zhao, J., & Zhao, M. (2023). Preparation and properties of calcium aluminate cement with Bayer red mud. Construction and Building Materials, 373, Article 130827. https://doi.org/10.1016/j.conbuildmat.2023.130827
Hou, D., Wu, D., Wang, X., Gao, S., Yu, R., Li, M., Wang, P., & Wang, Y. (2021). Sustainable use of red mud in ultra-high performance concrete (UHPC): Design and performance evaluation. Cement and Concrete Composites, 115, Article 103862. https://doi.org/10.1016/j.cemconcomp.2020.103862
Hyeok-Jung, K., Kang, S. P., & Choe, G. C. (2018). Effect of red mud content on strength and efflorescence in pavement using alkali-activated slag cement. International Journal of Concrete Structures and Materials, 12, Article 18. https://doi.org/10.1186/s40069-018-0248-2
Kang, S. P., & Kwon, S. J. (2017). Effects of red mud and alkali-activated slag cement on efflorescence in cement mortar. Construction and Building Materials, 133, 459–467. https://doi.org/10.1016/j.conbuildmat.2016.12.071
Kostrzewa-Demczuk, P., Stepien, A., Dachowski, R., & da Silva, R. B. (2023). Influence of waste basalt powder addition on the microstructure and mechanical properties of autoclave brick. Materials, 16(2), Article 870. https://doi.org/10.3390/ma16020870
Krivenko, P., Kovalchuk, O., Pasko, A., Croymans, T., Hult, M., Lutter, G., Vandevenne, N., Schreurs, S., & Schroeyers, W. (2017). Development of alkali activated cements and concrete mixture design with high volumes of red mud. Construction and Building Materials, 151, 819–826. https://doi.org/10.1016/j.conbuildmat.2017.06.060
Li, X., Zhang, Q., Mao, S., Li, L., & Wang, J. (2019). Study on the preparation and fracture behavior of red mud-yellow phosphorus slag-based concrete. Advances in Materials Science and Engineering, 2019, 1–15. https://doi.org/10.1155/2019/5370073
Liang, L., Du, X., Gao, X., Wang, Y., Zhang, J., Xue, X., Shi, S., Su, N., Zhang, K., & Li, G. (2023). Construction and optimization of Fe3O4/C/ceramic composite absorbents by one-step recycling red mud and coal hydrogasification residue. Materials Today Communications, 34, Article 105303. https://doi.org/10.1016/j.mtcomm.2023.105303
Liu, C., Wu, H., Jiang, J., Wang, L., Kong, D., & Yu, K. (2023). Properties of flue gas desulphurization gypsum–activated steel slag fine aggregate red mud–based concrete. Journal of Materials in Civil Engineering, 35(4), Article 04023025. https://doi.org/10.1061/JMCEE7.MTENG-14568
Liu, Z., Zhang, S., Hu, D., Zhang, Y., Lv, H., Liu, C., Chen, Y., & Sun, J. (2019). Paraffin/red mud phase change energy storage composite incorporated gypsum-based and cement-based materials: Microstructures, thermal and mechanical properties. Journal of Hazardous Materials, 364, 608–620. https://doi.org/10.1016/j.jhazmat.2018.10.051
Neves, A., Almeida, J., Cruz, F., Miranda, T., Cunha, V. M. C. F., Rodrigues, M., Costa, J., & Pereira, B. EB. (2023). Design procedures for sustainable structural concretes using wastes and industrial by-products. Applied Sciences, 13(4), Article 2087. https://doi.org/10.3390/app13042087
Nikbin, I. M., Aliaghazadeh, M., Charkhtab, S., & Fathollahpour, A. (2018). Environmental impacts and mechanical properties of lightweight concrete containing bauxite residue (red mud). Journal of Cleaner Production, 172, 2683–2694. https://doi.org/10.1016/j.jclepro.2017.11.193
Oltulu, M., & Alameri, I. (2019). The mechanical properties of concrete with red mud (bauxite residue) and nano-Al2O3 at high temperatures. Fresenius Environmental Bulletin, 28(6), 4692–4701.
Ortega, J., Cabeza, M., Tenza-Abril, A., Real-Herraiz, T., Climent, M., & Sánchez, I. (2019). Effects of red mud addition in the microstructure, durability and mechanical performance of cement mortars. Applied Sciences, 9(5), Article 984. https://doi.org/10.3390/app9050984
Pei, J., Pan, X., Wang, Y., Lv, Z., Yu, H., & Tu, G. (2023). Effects of alkali and alkaline-earth oxides on preparation of red mud based ultra-lightweight ceramsite. Ceramics International, 49(11), 18379–18387. https://doi.org/10.1016/j.ceramint.2023.02.199
Qureshi, H. J., Ahmad, J., Majdi, A., Saleem, M. U., Al Fuhaid, A. F., & Arifuzzaman, M. (2022). A study on sustainable concrete with partial substitution of cement with red mud: A review. Materials, 15(21), Article 7761. https://doi.org/10.3390/ma15217761
Ribeiro, D. V., Silva, A. S., Labrincha, J. A., & Morelli, M. R. (2013). Rheological properties and hydration behavior of portland cement mortars containing calcined red mud. Canadian Journal of Civil Engineering, 40(6), 557–566. https://doi.org/10.1139/cjce-2012-0315
Sruthi, S., & Gayathri, V. (2023). Synthesis and evaluation of eco-friendly, ambient-cured, geopolymer-based bricks using industrial by-products. Buildings, 13(2), Article 510. https://doi.org/10.3390/buildings13020510
Tang, W. C., Wang, Z., Liu, Y., & Cui, H. Z. (2018). Influence of red mud on fresh and hardened properties of self-compacting concrete. Construction and Building Materials, 178, 288–300. https://doi.org/10.1016/j.conbuildmat.2018.05.120
Tang, W. C., Wang, Z., Donne, S. W., Forghani, M., & Liu, Y. (2019). Influence of red mud on mechanical and durability performance of self-compacting concrete. Journal of Hazardous Materials, 379, Article 120802. https://doi.org/10.1016/j.jhazmat.2019.05.120
Turkish Standards Institution. (2016a). Methods of testing cement - Part 1: Determination of strength (TS EN 196-1). Ankara, Türkiye.
Turkish Standards Institution. (2016b). Cement - Composition, specifications and conformity criteria for common cements (TS EN 197-1). Ankara, Türkiye.
Turkish Standards Institution. (2014). Concrete - Specification, performance, production, and conformity (TS EN 206). Ankara, Türkiye.
Turkish Standards Institution. (2019). Testing hardened concrete - Part 3: Compressive strength of test specimens (TS EN 12390-3). Ankara, Türkiye.
Turkish Standards Institution. (2010). Testing hardened concrete - Part 6: Tensile splitting strength of test specimens (TS EN 12390-6). Ankara, Türkiye.
Vedaiyan, B., & Govindarajalu, E. (2023). A multi-objective robust grey wolf optimization model for the study of concrete mix using copper slag and glass powder. The International Journal of Advanced Manufacturing Technology, 125(3), 1941–1953. https://doi.org/10.1007/s00170-022-10326-4
Venkatesh, C., Nerella, R., & Chand, M. S. R. (2019). Comparison of mechanical and durability properties of treated and untreated red mud concrete. Materials Today: Proceedings, 27, 284–287. https://doi.org/10.1016/j.matpr.2019.11.025
Venkatesh, C., Nerella, R., & Chand, M. S. R. (2020). Experimental investigation of strength, durability, and microstructure of red-mud concrete. Journal of the Korean Ceramic Society, 57(2), 167–174. https://doi.org/10.1007/s43026-020-00046-y
Verma, N. K., Meesala, C. R., & Kumar, S. (2023). Developing an ANN prediction model for compressive strength of fly ash-based geopolymer concrete with experimental investigation. Neural Computing and Applications, 35(14), 10329–10345. https://doi.org/10.1007/s00521-022-08065-1
Wang, L., Chen, L., Guo, B., Tsang, D. C. W., Huang, L., Ok, Y. S., & Mechtcherine, V. (2020). Red mud-enhanced magnesium phosphate cement for remediation of Pb and As contaminated soil. Journal of Hazardous Materials, 400, Article 123317. https://doi.org/10.1016/j.jhazmat.2020.123317
Wang, Y., & Zhen, Z. (2024). Properties of red-mud-modified basic magnesium sulfate cement. Materials, 17(16), Article 4085. https://doi.org/10.3390/ma17164085
Yavuz, D. (2024). Freeze-thaw and drop-weight impact resistance of fiber-reinforced pervious concretes produced using recycled pervious concrete aggregate. Challenge Journal of Structural Mechanics, 10(4), 138–148.
Yuan, B., Yuan, S., Straub, C., & Chen, W. (2020). Activation of binary binder containing fly ash and portland cement using red mud as alkali source and its application in controlled low-strength materials. Journal of Materials in Civil Engineering, 32(2), Article 04019356. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003051
Zhu, J., Yue, H., Ma, L., Li, Z., & Bai, R. (2023). Study on hydration mechanism and environmental safety of thermal activated red mud-based cementitious materials. Environmental Science and Pollution Research, 30(21), 55905–55921. https://doi.org/10.1007/s11356-023-26245-1